Coatings, Vol. 13, Pages 1054: Research on the Influence of Coating Technologies on Adhesion Anti-Corrosion Layers in the Case of Al7175 Aluminum Alloy

Coatings, Vol. 13, Pages 1054: Research on the Influence of Coating Technologies on Adhesion Anti-Corrosion Layers in the Case of Al7175 Aluminum Alloy

Coatings doi: 10.3390/coatings13061054

Authors: Titu Ravai-Nagy Pop

A key element in ensuring the service life and strength of aluminum alloys in many industrial applications is the adhesion of anti-corrosion coatings. The aim of this study is to analyze how coating processes affect the adhesion of anti-corrosion coatings on aluminum alloy 7175. In other words, the influence of the nature of the elementary layers that form the anti-corrosion coating was studied for the following: the anodic layer, the primer, and the topcoat. To learn more about the different coating technologies and how they affect adhesion, a thorough literature review was carried out. In addition, a case study using electrocoating and thermal spraying was conducted to show the impact of coating processes on adhesion. The results showed that electrodeposition, as opposed to thermal spraying, improved the adhesion of anti-corrosion coatings. In the case of the aluminum alloy analyzed, there is a significant difference in terms of the adhesion strength of the anti-corrosion coatings. This resistance is influenced by both the anodic coating (BSA TSA SAA) and the type of primer and topcoat used (water-based or solvent-based). The correct choice of anode coat and primer and topcoat can lead to an increase (or decrease) in the adhesion strength of the paint coat by 20%. In conclusion, this study highlights how crucial it is to select the best coating process to maximize the adhesion and durability of aluminum alloys under corrosion conditions.