Coatings, Vol. 13, Pages 953: The Electrodeposition of Derivatives of Pyrrole and Thiophene on Brass Alloy in the Presence of Dodecane-1-Sulfonic Acid Sodium Salt in Acidic Medium and Its Anti-Corrosive Properties

Coatings, Vol. 13, Pages 953: The Electrodeposition of Derivatives of Pyrrole and Thiophene on Brass Alloy in the Presence of Dodecane-1-Sulfonic Acid Sodium Salt in Acidic Medium and Its Anti-Corrosive Properties

Coatings doi: 10.3390/coatings13050953

Authors: Florina Branzoi Simona Petrescu

In this paper, potentiostatic and galvanostatic deposition (electrochemical deposition) processes have been used for the obtained of a new composite polymer: N-methylpyrrole-sodium 1-dodecanesulfonate/poly 2-methylthiophene (PNMPY-1SSD/P2MT) coatings over brass electrode for corrosion protection. The sodium 1-dodecanesulfonate as a dopant ion employed in the electropolymerization procedure can have a meaningful effect on the anti-corrosion protection of the composite polymeric film by stopping the penetration of corrosive ions. The composite coatings have been characterized by cyclic voltammetry, Fourier transform infrared (FT-IR) spectroscopy, and scanning electron microscopy (SEM) procedures. The anti-corrosion performance of PNMPY-1SSD/P2MT coated brass has been investigated by potentiostatic and potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) practices in 0.5 M H2SO4 medium. The corrosion assessment of PNMPY-1SSD/P2MT coated brass was noticed to be ~9 times diminished than of uncoated brass, and the efficiency of these protective coatings of this coating is above 90%. The highest effectiveness is realized by the electrochemical deposition of PNMPY-1SSD/P2MT obtained at 1.1 V and 1.4 V potential applied and at 0.5 mA/cm2 and 1 mA/cm2 current densities applied in molar ratio 5:3. The outcomes of the corrosion tests denoted that PNMPY-1SSD/P2MT coatings assure good anti-corrosion protection of brass in corrosive media.