Crystals, Vol. 14, Pages 686: Analysis of the Anisotropic Cyclic Material Behavior of EN AW-1050A H24 Derived from Strain-Controlled Testing Using a Clip-On Extensometer and an Optical System
Crystals doi: 10.3390/cryst14080686
Authors: Tim Korschinsky Benjamin Möller Marvin Kiel Matthias Hecht
Due to its good conductive properties, unalloyed (pure) aluminum, such as EN AW-1050A H24, finds new fields of application in electromobility. To optimize components, the cyclic material behavior must be understood and described precisely as a foundation of a proper fatigue life estimation. Various cyclic tests were performed to not only derive the cyclic parameters to describe the material but also to find the most suitable procedure to deal with the challenges faced during the experiments. The main point of interest is the comparison between a surface-mounted clip-on extensometer and an optical system both used for strain control in cyclic tests. For the analysis of the anisotropic behavior of EN AW-1050A H24, un-notched flat specimens were extracted from sheet metal lengthways and crossways in respect to the rolling direction. While the cyclic material behavior for specimens of both directions of extraction is characterized by cyclic softening in general, the specimens extracted crossways show a strain-amplitude-dependent cyclic softening with strong strain localization especially at the contact points of the knives of the clip-on extensometer leading to an increased quantity of invalid experiments as well as sudden fractures. In the study, it was possible to show the benefits of a contactless optical strain control system when dealing with very soft metallic materials such as EN AW-1050A H24.