Materials, Vol. 16, Pages 2711: Surface Treatment of Mongolian Scots Pine Using Phosphate Precipitation for Better Performance of Compressive Strength and Fire Resistance

Materials, Vol. 16, Pages 2711: Surface Treatment of Mongolian Scots Pine Using Phosphate Precipitation for Better Performance of Compressive Strength and Fire Resistance

Materials doi: 10.3390/ma16072711

Authors: Yan Ge Liang Wang Xuepeng Wang Hao Wang

Wood, as a naturally green and environmentally friendly material, has been widely used in the construction and decoration industries. However, the flammability of wood poses serious safety problems. To improve the fire resistance of wood, In this study, it is proposed to use calcium chloride (CaCl2) and disodium hydrogen phosphate (Na2HPO4, DSP) to impregnate wood for multiple cycles. The experimental results show that phosphate mineral precipitation can be deposited on the surface of the wood. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) are used to analyze the micromorphology of mineral precipitation and use the MIP test to analyze the treated wood pore structure. The results show that with the increase in the number of cycles, the phosphate deposited on the surface of the wood increases, and the cumulative pore volume and water absorption rate of the wood after 10 cycles are 54.3% and 13.75% lower than that of untreated wood respectively. In addition, the cone calorimeter (CONE) confirmed that the total heat release (THR) and total smoke production (TSP) of wood treated in 10 cycles have decreased by 48.7% and 54.2% respectively compared with the untreated wood. Hence, this treatment method not only improves the mechanical properties of wood. It also improves fire resistance.