Materials, Vol. 16, Pages 4214: Development of Pore Pressure in Cementitious Materials under Low Thermal Effects: Evidence from Optimization of Pore Structure by Incorporation of Fly Ash

Materials, Vol. 16, Pages 4214: Development of Pore Pressure in Cementitious Materials under Low Thermal Effects: Evidence from Optimization of Pore Structure by Incorporation of Fly Ash

Materials doi: 10.3390/ma16124214

Authors: Wei Jiang Dandan Zhang Xinyue Zheng Wenqian Li

Studies on durability of cementitious materials have focused on harsh environments, but less attention has been paid to low thermal loading situations. In this paper, with the aim of exploring the evolution of internal pore pressure and microcrack extension of cementitious under low thermal environment, cement paste specimens with thermal environment slightly below 100 °C and three water–binder ratios (0.4, 0.45 and 0.5) and four fly ash admixtures (0, 10%, 20% and 30%) were designed. Firstly, the internal pore pressure of the cement paste was tested; secondly, the average effective pore pressure of the cement paste was calculated; and finally, the phase field method was used to explore the expansion of microcracks inside the cement paste when the temperature gradually increased. It was found that the internal pore pressure of the paste showed a decreasing trend as the water–binder ratio and fly ash admixture increased, and the numerical simulation found that the sprouting and development of cracks were delayed when 10% fly ash was added to the cement paste, which was consistent with the experimental results. This work provides a basis for the durability development of concrete under low thermal environment.