Materials, Vol. 16, Pages 986: Removal of Sodium from Vanadium Tailings by Calcification Roasting in Reducing Atmosphere

Materials, Vol. 16, Pages 986: Removal of Sodium from Vanadium Tailings by Calcification Roasting in Reducing Atmosphere

Materials doi: 10.3390/ma16030986

Authors: Wang Guo Wang Chen Yang Zheng

Vanadium tailings from vanadium extraction by a sodium roasting process are solid waste and cannot be used in sintering and ironmaking due to their high sodium content. In this paper, a calcification and reduction roasting process was proposed to remove sodium from vanadium tailings. The effects of Ca(OH)2 addition, reduction temperature, and roasting time on the sodium removal behavior and compression strength of pellets were studied. The addition of Ca(OH)2 and the reduction of iron oxides promoted the sodium-containing phases to transform to be simpler, which could enhance sodium removal. The sodium removal rate was up to 93.47% and the compression strength of the reduced products was 4497 N/P, and the metallized ratio of the product was higher than 70% under the optimal conditions: roasting at 1200 °C for 2 h with the Ca(OH)2 addition of 35%. The treated product after removing sodium can be recycled in the ironmaking process in a steel company.