Materials, Vol. 17, Pages 3366: Three-Dimensional Printing of Yttrium Oxide Transparent Ceramics via Direct Ink Writing

Materials, Vol. 17, Pages 3366: Three-Dimensional Printing of Yttrium Oxide Transparent Ceramics via Direct Ink Writing

Materials doi: 10.3390/ma17133366

Authors: Qiming Chen Huibing Li Weijie Han Jian Yang Wentao Xu Youfu Zhou

The utilization of 3D printing technology for the fabrication of intricate transparent ceramics overcomes the limitations associated with conventional molding processes, thereby presenting a highly promising solution. In this study, we employed direct ink writing (DIW) to prepare yttrium oxide transparent ceramics using a ceramic slurry with excellent moldability, solid content of 45 vol%, and shear-thinning behavior. A successfully printed transparent yttrium oxide ring measuring 30 mm in diameter, 10 mm in inner diameter, and 0.9 mm in thickness was obtained from the aforementioned slurry. After de-binding and sintering procedures, the printed ceramic exhibited in-line transmittance of 71% at 850 nm. This work not only produced complex yttria transparent ceramics with intricate shapes, but also achieved in-line transmittance that was comparable to that of the CIP method (79%), which can meet certain optical applications.