Minerals, Vol. 13, Pages 133: The Self-Reduction during the Thermal Decomposition of an Ammonium Molybdate

Minerals, Vol. 13, Pages 133: The Self-Reduction during the Thermal Decomposition of an Ammonium Molybdate

Minerals doi: 10.3390/min13020133

Authors: Kyoungkeun Yoo Won Beom Koo Hanggoo Kim Sang-hun Lee

In the hydrometallurgical process of molybdenum using ammonia solution, ammonium paramolybdate tetrahydrate (APT: (NH4)6Mo7O24·4H2O) is produced as an intermediate product after a crystallization step. ATP is then thermally decomposed at a high temperature to give MoO3, which is reduced by hydrogen gas in a two-stage process to reduce molybdenum metal powder as the final product. If APT is pre-dried at an appropriately low temperature to remove the crystal water corresponding to 4 mol per mol of APT, it changes into (NH4)4Mo5O17, and the content of residual ammonia, which can be utilized as a reductant, in the ammonium molybdate increases. In this regard, the self-reducing potential of (NH4)4Mo5O17 was examined in this study through the effectiveness analysis of the residual ammonia component as a reductant for the primary hydrogen reduction step. In a series of experimental work on the thermal decomposition of (NH4)4Mo5O17 in an inert atmosphere, a maximum self-reduction degree of 18% was achieved. Based on this result, it can be expected that the metal powder can be manufactured in a more effective way than conventional processes in terms of hydrogen consumption and reaction time.